| Description |
Test Methods |
Units |
Fast Cure |
Standard Cure |
| Solar-F-A |
Solar-F-B |
Solar-S |
| Properties |
- |
- |
Ultra High Light Transmission |
Ultra High Light Transmission & Significant Anti-Aging |
General Applications |
| Density |
ISO 1183 |
g/cm3 |
0.96 |
0.96 |
0.96 |
| Tensile Strength |
ISO 527-3 |
MPa |
16 |
16 |
16 |
| Elongation at Break |
% |
550 |
550 |
550 |
| Young’s Modulus (Cured) |
MPa |
4.7 |
4.7 |
4.7 |
| Hardness |
GB/T531-1999 |
Shore A |
72 ~ 75 |
72 ~ 75 |
72 ~ 75 |
| Optical Transmission (390~1105nm) |
ASTM D1003 |
% |
＞92 |
＞92 |
＞92 |
| Refractive Index |
ISO 489 |
- |
1.481 |
1.481 |
1.481 |
| UV Cutoff Wavelength |
UV-Vis |
Nm |
310 |
360 |
|
| UV Light Resistance (280nm~385nm, 15KWh/m2) |
|
% Transmission Retention |
＞88 |
＞90 |
＞88 |
| Heat/Humidity Resistance (85℃/85RH, 2000 hrs) |
Q/HZF 001-2006 |
＞88 |
＞88 |
＞88 |
| Cross-Linking Rate |
Gel % |
75 ~ 85 |
80 ~ 90 |
75 ~ 85 |
| Strength Peeling (Glass) |
N/cm |
＞60 |
＞60 |
＞60 |
| Strength Peeling (TPT) |
N/cm |
＞40 |
＞40 |
＞40 |
| Shrinkage Rate (120℃, 3 Min.) |
MD / TD % |
＜4 / ＜2 |
＜4 / ＜2 |
＜4 / ＜2 |
| Water Absorbing Rate |
GB/T1034-1998 |
% |
＜0.1 |
＜0.1 |
＜0.1 |
| Volume Insulating Resistance |
GB/T1410-2006 |
MΩ |
1.45 x 106 |
1.45 x 106 |
1.45 x 106 |
| Range of Thickness |
GB/T6672-2001 |
mm |
0.3 ~ 0.8 |
0.3 ~ 0.8 |
0.3 ~ 0.8 |
| Range of Width |
NA |
mm |
250 ~ 2000 |
250 ~ 2000 |
250 ~ 2000 |