| Models |
Applications |
Curing Method |
Curing Time |
Viscosity |
Properties |
| LRGL-JB |
Budget Resin for General Purpose
 |
UV |
25 ~ 40 min. (mW/cm2) |
Low |
- 5 Years Anti-Aging
- Suitable for General Applications
- Fulfill China National Standard GB9962-1999
|
| Heat |
85℃ for 8 hrs |
Low |
| LRGL-BL |
Splinter Pattern for Decoration
 |
UV |
25 ~ 40 min. (mW/cm2) |
Low |
- 5 Years Anti-Aging
- High Elasticity & Elongation
- Suitable to Laminate Temper Glass & Break into Cracking Visual Effect
- Fulfill China National Standard GB9962-1999
|
| LRGL-S |
High Performance for General Purpose
 |
UV |
30 ~ 35 min. (mW/cm2) |
Slightly Low |
- 10 Years Anti-Aging
- Strong Adhesion
- High Impact Strength
- High Elasticity
- Low Shrinkage
- Fast Curing Time
- Ultra High Transparency
- Fulfill China National Standard GB9962-1999
|
| Heat |
85℃ for 8 hrs |
Slightly Low |
| LRGL-A |
Sound Barrier
 |
UV |
30 ~ 35 min. (mW/cm2) |
Slightly Low |
- 10 Years Anti-Aging
- Soft Resin Interlayer
- Excellent in Noise Reduction
- General Impact Strength
- Fulfill EN ISO-12543-4 Anti-Aging Test
|
| LRGL-H |
High Impact Resistance
 |
UV |
20 ~ 25 min. (mW/cm2) |
Slightly High |
- 10 Years Anti-Aging
- Excellent Impact Strength
- Excellent Toughness
- Excellent Adhesion
- Low Shrinkage
- Fulfill EN356 Steel Ball Drop Test & Axe Penetration Test
- Fulfill EN ISO-12543-4 Anti-Aging Test
|
| LRGL-B |
Bullet Proof
 |
UV |
20 ~ 25 min. (mW/cm2) |
High |
- Highest Impact Strength
- Highest Toughness
- Excellent Adhesion
- Low Shrinkage
- Fulfill EN1063 Bullet Resistant Test
- Fulfill ISO-12543-4 Anti-Aging Test
|